| DINALON®PA 6.6 30% FV is a polyamide 66 (nylon 66) product, which contains 30% glass fiber reinforcement. It can be processed by injection molding and is available in Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 180 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 7500 | MPa | ASTM D790 |
| Flexural Strength | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 250 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Glow Wire, UNE 20-672-83: 650°CVicat Softening Temperature, ASTM D1525: >250°CDTUL, ASTM D648: 225°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 85.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Regis® E6426 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| Moplen HP741H | LyondellBasell Industries | PP Homopolymer | Moplen |
| DIALAC® S351 | UMG ABS, Ltd. | SAS | DIALAC® |
| Formolene® 4142R | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| PolyFibra® PF-PHF04 | FuturaMat | PP, Unspecified | PolyFibra® |