TITANEX® HF1881
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Lotte Chemical Titan (M) Sdn. Bhd. |
| Trademark: | TITANEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pxVCUy_TITANEX-HF1881.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HF1881 is a pelleted medium molecular weight, high density polyethylene Hexene-1 resin for tubular film extrusion. HF1881 meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 3.1a & 3.2a. APPLICATIONS: Grocery sacks, shopping bags, liners and thin films. Characteristics: Specially designed for high extrusion rate at lower temperature, good film strength and rigidity, excellent drawdown for high quality thin film, when better strength is needed, mixing with HF0961 will provide a balance between strength and extrudability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | |
| 190°C/21.6 kg | 18 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 17 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 17 µm, Blown Film | 912 | MPa | |
| 1% Secant, TD : 17 µm, Blown Film | 932 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 17 µm, Blown Film | 53.9 | MPa | |
| TD : Break, 17 µm, Blown Film | 39.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 17 µm, Blown Film | 350 | % | |
| TD : Break, 17 µm, Blown Film | 500 | % | |
| Dart Drop Impact (17 µm, Blown Film) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 17 µm, Blown Film | 5.1 | g | |
| TD : 17 µm, Blown Film | 68 | g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoPet 3510 | TechnoCompound GmbH | PET | TechnoPet |
| Taitarex® 866NM / BM | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |
| Hylon® N1040MG25HLUV2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| IPC PP 4830H-T | International Polymers Corporation | PP Homopolymer | IPC PP |
| EPALINE 786A34 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPALINE |