NOVADYN™ DT
| Category: | HPPA , High Performance Polyamide |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | NOVADYN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pxAnHg_NOVADYN-DT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INVISTA's Novadyn™ DT is made from DYTEK® A diamine and purified terephthalic acid (PTA). |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 78 | -- | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | 3210 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 97.0 | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield, 23°C | 7.2 | 6.3 | % | |
| Break, 23°C | 34 | 6.3 | % | |
| Flexural Modulus 1(23°C) | 2900 | 2900 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 92.0 | 129 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 4.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 | 58 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 7.8 | 3.9 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 24 | 38 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 132 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 117 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 3 | 147 | -- | °C | DSC |
| Melting Temperature 4 | 295 | -- | °C | DSC |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Moisture Absorption - After conditioning 5 | -- | 3.9 | % | ISO 1110 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 275 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 300 | °C | |
| Nozzle Temperature | 310 | °C | |
| Mold Temperature | 85.0 | °C | |
| Back Pressure | 0.500 | MPa | |
| Screw Speed | 125 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 20°C/min |
| 4 . | 20°C/min |
| 5 . | Conditioned at 70°C, 62% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylite® Profile™ 33541-00 | Reichhold Chemicals, Inc. | Polyester, TS | Polylite® Profile™ |
| UBE Nylon 1022 C2 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| GPP™ 1001V0M | S&E Specialty Polymers, LLC | TPO (POE) | GPP™ |
| Karina IVORY PVC COMPOUND 809D35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ XHT1171 resin | SABIC Innovative Plastics | PC | LEXAN™ |