Karina BLACK PVC COMPOUND 70900-48/1-E-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | px41S0_Karina-BLACK-PVC-COMPOUND-70900-48-1-E-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND CLASS 70C (PVC/A) RECOMMENDED FOR INSULATION OF ELECTRICAL WIRES AND CABLES (BW). |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.44 to 1.50 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -0.830 to 0.770 | ME 12 | |
| Color b | -1.24 to 0.360 | ME 12 | |
| Color L | 26.0 to 27.6 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 90 to 94 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 3.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vexel 120GF30 FR | Custom Resins Group | PBT | Vexel |
| 3M™ Dyneon™ PTFE TF 9201Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Celstran® +PP-GF40-04CN03/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Geon™ Vinyl Flexible D7000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| TECHNYL STAR® S 218 V35 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |