Latigloss 62 H2 G/50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigloss |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pwfwF2_Latigloss-62-H2-G-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.20 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 14500 | MPa | |
| 60°C | 10500 | MPa | |
| 90°C | 6500 | MPa | |
| 120°C | 5200 | MPa | |
| 150°C | 5000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 200 | MPa | |
| Break, 60°C | 140 | MPa | |
| Break, 90°C | 85.0 | MPa | |
| Break, 120°C | 65.0 | MPa | |
| Break, 150°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.8 | % | |
| Break, 60°C | 4.0 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 8.0 | % | |
| Break, 150°C | 9.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BULKSAM® NTV25 | UMG ABS, Ltd. | ABS | BULKSAM® |
| ASTALOY™ PC/ABS M130S | Marplex Australia Pty. Ltd. | PC+ABS | ASTALOY™ |
| Chiao Fu PA6 MC312GM25 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| DELPET™ PM120N | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |