DILAMID® 6 SV 30 NATURAL OR BLACK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Dilaplast S.p.A. |
| Trademark: | DILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pwIATQ_DILAMID-6-SV-30-NATURAL-OR-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DILAMID® 6 SV 30 NATURAL OR BLACK is a Polyamide 6 (Nylon 6) material filled with 30% glass bead. It is available in Europe for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.0 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 3.60 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 2.0 to 8.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 255 to 295 | °C | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205H TFE 13 SI 2 | RTP Company | Nylon 66 | RTP |
| Miramid® TE30CW | BASF Leuna GmbH | Nylon 66/6 | Miramid® |
| FHR Polypropylene P9M7R-056 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| LNP™ LUBRILOY™ Z20001 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRILOY™ |
| Axiall PVC 9275 J | Axiall Corporation | PVC, Rigid | Axiall PVC |