LNP™ STAT-KON™ DDF029 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pvaiRc_LNPSTATKONDDF029compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant, Glass Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound DF-FR Product reorder name: DDF029 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.49 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.44 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4480 | MPa | ASTM D638 |
| -- | 4600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 81.9 | MPa | ASTM D638 |
| Fracture | 81.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.9 | % | ASTM D638 |
| Fracture | 2.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4410 | MPa | ASTM D790 |
| -- | 4800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 133 | MPa | ASTM D790 |
| -- | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.30 | J | ASTM D3763 |
| -- | 2.27 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 136 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 135 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 - 1.0E+10 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-TK200 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| Taitacell EPS 391Ss | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Boda BDF-H2601 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Elastron® G G101.A65.B.E | Elastron USA, Inc. | SEBS | Elastron® G |
| OpteSTAT™ BP 1100 | Ovation Polymers Inc. | TP, Unspecified | OpteSTAT™ |