Therma-Tech™ TT9200-5010 EC Anthracite
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Therma-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | puiivo_ThermaTechTT92005010ECAnthracite.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.79 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (Injection Molded) | 0.10 - 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 17500 | MPa | ISO 527 |
| Tensile Stress (Break) | 64.0 | MPa | ISO 527-2/1/50 |
| Tensile Elongation 2(Break) | 0.30 - 0.50 | % | ISO 527 |
| Flexural Modulus 3(Injection Molded) | 16000 | MPa | ISO 178 |
| Flexural Strength 4(Injection Molded) | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 6.3 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | °C | ISO 75-2/A |
| Thermal Conductivity 5 | 2.0 - 2.4 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | V-0 | UL 94 | |
| 1.5 mm | 5VA | UL 94 | |
| 3.0 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.8 mm | 960 | °C | IEC 60695-2-12 |
| 1.6 mm | 960 | °C | IEC 60695-2-12 |
| 3.0 mm | > 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.6 mm | > 960 | °C | IEC 60695-2-13 |
| 3.0 mm | > 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 310 - 340 | °C | |
| Mold Temperature | 140 - 170 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 1.0mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | Through Plane with Modified Transient Plane Source technique, C-Therm TCi™ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 3721WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| China PPS PTFE-hCF313 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Jackdaw PC DS10NT6539 | Jackdaw Polymers | PC | Jackdaw PC |
| OnFlex™ S EH 70A-3S7004 | PolyOne Corporation | TPE | OnFlex™ |
| ROTOLENE® Black Total Plus | Polimeros Mexicanos S.A. de C.V. | LMDPE | ROTOLENE® |