Latan 13 G/30
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pucXpk_Latan-13-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyoximethylene (POM). Glass fibres. Medium viscosity. Good tribological properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 0.45 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 7500 | MPa | |
| 60°C | 5900 | MPa | |
| 90°C | 4000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 100 | MPa | |
| Break, 60°C | 85.0 | MPa | |
| Break, 90°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 3.0 | % | |
| Break, 60°C | 4.0 | % | |
| Break, 90°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 85.0 | °C | |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4702-698UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| ExxonMobil™ SFT325 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| LNP™ STAT-KON™ RE007 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Durez® M75202 | SBHPP | Phenolic | Durez® |
| TECACOMP® PPA TRM XS black 4173 | Ensinger GmbH | PPA | TECACOMP® |