FRblend® PP-1309
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | puaQwz_FRblend-PP-1309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PP-1309 is a low flow, glass and mineral filled, flame retardant polypropylene mineral filled compound. This grade offers high rigidity, high toughness and good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10100 | MPa | ASTM D638 |
| Tensile Strength | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 7940 | MPa | ASTM D790 |
| Flexural Strength | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 140 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 210 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE Compound TF 4103 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Cheng Yu E2345 | Cheng Yu Plastic Company Limited | PET | Cheng Yu |
| EMLON® 66 GFR 30 FR V0 | EMAS Plastik San.Tic.AS. | Nylon 66 | EMLON® |
| Jampilen HP562S | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Polifil® PP C-10 | The Plastics Group | PP Homopolymer | Polifil® PP |