EPIMIX POM IMP NC B501
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ptzkVr_EPIMIX-POM-IMP-NC-B501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYACETAL POM, with improved good-impact resistance , Standard-flow grad, for injection molding. POLYACETAL POM , is used in all sectors of industry, compliance with RoHs derivatives. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.31 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 9.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.8 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 1.4 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.25 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 76 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | 1650 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 40.0 | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | < 50 | < 40 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1700 | 1550 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 70.0 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 8.0 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 12 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 80.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 160 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 160 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® ECO P10P | Tekni-Films, a div of Tekni-Plex | Film, PP/COC/EVOH/PP | TEKNIFLEX® ECO |
| Yuyao PBT 518 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| NYCOA Polyamide 2046 | Nycoa (Nylon Corporation of America) | Nylon 6/69 | NYCOA Polyamide |
| Cheng Yu T889G25 | Cheng Yu Plastic Company Limited | PBT | Cheng Yu |
| SQUARE® LIM1030-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |