TAISOX 2125
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pttU1F_TAISOX-2125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 2125 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is: cast film. The main characteristics of TAISOX 2125 are puncture resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm, cast film | 177 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm, cast film | 167 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm, extruded film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 20 µm, extruded film | 10.8 | MPa | ASTM D882 |
| MD : Fracture, 20 µm, extruded film | 32.4 | MPa | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 24.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 20 µm, extruded film | 540 | % | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 710 | % | ASTM D882 |
| Dart Drop Impact (20 µm, Cast Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, cast film | 210 | g | ASTM D1922 |
| TD : 20 µm, cast film | 460 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 121 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 96 | ASTM D2457 | |
| Clarity | 95.0 | ASTM D1746 | |
| Haze (20.0 µm, Cast Film) | 3.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SC204 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Spartech Polycom PP5340 B2 | Spartech Polycom | PP, Unspecified | Spartech |
| Staramide PX08000 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Thermoset Plastics SC-134 | Thermoset, Lord Chemical Products | Silicone | Thermoset Plastics |
| WanBlend® WHT-8190M | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |