XANTAR® C RC 3012
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ptZGOl_XANTAR-C-RC-3012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General purpose, Vicat 120°C |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/4A | ||
| -40°C | 35 | kJ/m² | |
| -20°C | 55 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 109 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 124 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 22 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity of Melt | 0.23 | W/m/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC FK 0635 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ELIX™ ABS M305 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| ICORENE® N9203 | ICO Polymers EMEA, A Division of A. Schulman | PETG | ICORENE® |
| Plexiglas® Heatstop 8N black | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Sylvin 9077A-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |