ACCUCOMP™ POL051L
| Category: | PC , Polycarbonate |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ptRVQH_ACCUCOMP-POL051L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ POL051L is a Polycarbonate (PC) product. It is available in North America. Primary characteristic: medium viscosity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 70.0 | MPa | |
| Break | 70.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 110 | % | |
| Break | 150 | % | |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 900 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 140 | °C | |
| 1.8 MPa, Unannealed | 122 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP512D | Southern Polymer, Inc. | LDPE | PRIMALENE |
| Resiten® LEFBE | ITEN INDUSTRIES | Phenolic | Resiten® |
| Hybrid S464G10 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Lifoflex® UV 50 GB 1050 | ELASTO | SEBS | Lifoflex® |
| Wuxi Jiahong EB-2000 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |