CONTINUUM™ DGDA-2490 BK GL
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ptLdTX_CONTINUUM-DGDA-2490-BK-GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONTINUUM™ DGDA-2490 BK GL Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long-term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation is desired. Suitable applications include natural gas distribution pipes, industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ISO 1183 | ||
| Natural | 0.949 | g/cm³ | |
| Black | 0.959 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 7.5 | g/10 min | |
| 190°C/5.0 kg | 0.31 | g/10 min | |
| Carbon Black Content | 2.3 | % | ISO 6964 |
| Carbon Black Dispersion | < 3 | ISO 18553 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hydrostatic Strength | ISO 1167 | ||
| 1798 psi (12.4 MPa) : 20°C | > 200 | hr | |
| 725 psi (5.0 MPa) : 80°C | > 5000 | hr | |
| 783 psi (5.4 MPa) : 80°C | > 1000 | hr | |
| Resistance to Rapid Crack Propagation, Pc - S-4 (0°C) | > 12.0 | bar | ISO 13477 |
| Resistance to Rapid Crack Propagation, Tc - S-4 at 10 bar | < -17 | °C | ISO 13477 |
| Slow Crack Growth PENT - 348 psi (2.4 MPa) (80°C) | > 3000 | hr | ISO 16241 |
| Stress Crack Resistance - Notched Pipe Test (80°C) 1 | > 1000 | hr | ISO 13479 |
| Tensile Strength - for Butt-fusion | Test to failure: Ductile | ISO 13953 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time | > 20 | min | ISO 11357-6 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 24.1 | MPa | ISO 6259 |
| Tensile Strain (Break) | > 500 | % | ISO 6259 |
| Note Message | |
|---|---|
| 1 . | 133 psi (0.92 MPa), 110 mm SDR 11 pipe |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEDUR® L 9510-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| Sumiflex® K K530DA | Mitsubishi Chemical Corporation | PVC Elastomer | Sumiflex® K |
| SuperLite® SL552000-100 (6.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Fainplast PVC CKL 91/T-UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 7868-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |