LNP™ THERMOCOMP™ KF002L compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pslGwE_LNPTHERMOCOMPKF002Lcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF002L is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible. Also known as: LNP* THERMOCOMP* Compound KF-1002 LE Product reorder name: KF002L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.6 - 1.8 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.5 - 1.7 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.6 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.7 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6210 | MPa | ASTM D638 |
| -- | 5600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 66.2 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2 |
| Fracture | 63.4 | MPa | ASTM D638 |
| Fracture | 63.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.2 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Fracture | 3.4 | % | ASTM D638 |
| Fracture | 3.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4830 | MPa | ASTM D790 |
| -- | 4400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 3 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.40 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 163 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 162 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 155 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 148 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.4E-6 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENYL HT 2010 Y | Vamp Tech | PPA+Nylon | DENYL |
| EXTEM™ VH1003F resin | SABIC Innovative Plastics Asia Pacific | PEI | EXTEM™ |
| Geon™ Vinyl Rigid Extrusion L0152 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| INSULCAST® 3230 LV/INSULCURE 9 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| TechnoPet GF 20 2 1 | TechnoCompound GmbH | PET | TechnoPet |