VESTAMID® Care ML16
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® Care |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | psP9vC_VESTAMID-Care-ML16.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VESTAMID®Care ML grades cover a range of polyamide 12 resins of different viscosity for processing via extrusion or injection molding. The VESTAMID®Care ML product range consists of unstabilized base resins as well as stabilized or reinforced compounds. VESTAMID® Care ML resins are characterized by several outstanding properties, such as high impact & notched impact resistance, dimensional stability, good sliding properties, high abrasion resistance and resistance against chemicals. Unfilled VESTAMID® Care ML grades are for example the materials of choice for catheters and tubings, where VESTAMID® Care ML materials meet even highest challenges in applications such as angioplasty balloon catheters. Typical areas of application for reinforced VESTAMID® Care ML grades include housing-parts, monitoring and imaging devices and durable medical equipment. Due to their low water uptake, filled VESTAMID® Care ML grades even resist steam autoclaving for more than 500 cycles. The advantages at a glance :
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 | % | |
| Flow : 2.00 mm | 0.95 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.5 | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | % | |
| Viscosity Number | 120 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 5.0 | kJ/m² | |
| 23°C, Complete Break | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 170 | °C | ISO 306/A |
| -- | 140 | °C | ISO 306/B |
| Melting Temperature (DSC) 1 | 178 | °C | ISO 11357 |
| CLTE - Flow (23 to 55°C) | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SXXIC 9P BROWN | SRF Ltd. | Nylon 6 | TUFNYL® |
| TRILOY® 200NH | Samyang Corporation | PC+ABS | TRILOY® |
| Arak HDPE BL5 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Hifax CA 7378 A | LyondellBasell Industries | TPO (POE) | Hifax |
| Jampilen HP527J | Jam Polypropylene Company | PP Homopolymer | Jampilen |