Generic PEI
| Category: | PEI , Polyether Imide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | prc5Uw_Generic-PEI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PEI This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 - 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.27 - 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 8.1 - 19 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 7.00 - 56.7 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.49 - 0.64 | % | ASTM D955 |
| Transverse flow : 23°C | 0.59 - 0.61 | % | ASTM D955 |
| 23°C | 0.59 - 0.61 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.25 - 0.27 | % | ASTM D570 |
| 23°C, 24 hr | 0.29 - 0.30 | % | ISO 62 |
| Saturated, 23°C | 1.2 - 1.8 | % | ISO 62 |
| Equilibrium, 23°C | 1.2 - 1.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 - 0.72 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 109 - 110 | ASTM D785 | |
| Ball Indentation Hardness | 140 - 141 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2660 - 3780 | MPa | ASTM D638 |
| 23°C | 2780 - 3510 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 94.2 - 112 | MPa | ASTM D638 |
| Yield, 23°C | 92.5 - 113 | MPa | ISO 527-2 |
| Fracture, 23°C | 73.8 - 108 | MPa | ASTM D638 |
| Fracture, 23°C | 77.2 - 118 | MPa | ISO 527-2 |
| 23°C | 1.70 - 112 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.9 - 7.8 | % | ASTM D638 |
| Yield, 23°C | 5.8 - 8.6 | % | ISO 527-2 |
| Fracture, 23°C | 1.4 - 70 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 80 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2650 - 3560 | MPa | ASTM D790 |
| 23°C | 2700 - 3340 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 115 - 177 | MPa | ASTM D790 |
| 23°C | 106 - 166 | MPa | ISO 178 |
| Yield, 23°C | 135 - 174 | MPa | ASTM D790 |
| Fracture, 23°C | 141 - 160 | MPa | ASTM D790 |
| Compressive Modulus | 46.0 - 3390 | MPa | ASTM D695 |
| Compressive Strength (23°C) | 0.700 - 156 | MPa | ASTM D695 |
| Coefficient of Friction | 0.23 - 0.30 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 9.25 - 10.7 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.7 - 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 0.70 - 110 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 20 - 74 | J/m | ASTM D256 |
| 23°C | 3.7 - 6.3 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 1300 - 1400 | J/m | ASTM D256 |
| 23°C | 59 - 200 | kJ/m² | ISO 180 |
| Reverse Notch Izod Impact (23°C) | 2200 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C) | 24.8 - 43.5 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 22.9 - 36.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 204 - 237 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 194 - 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 196 - 230 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 184 - 228 | °C | ISO 75-2/A |
| Continuous Use Temperature | 170 - 171 | °C | ASTM D794 |
| Glass Transition Temperature | 194 - 233 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 218 - 242 | °C | ASTM D1525 |
| -- | 209 - 242 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 5.4E-5 - 5.6E-5 | cm/cm/°C | ASTM D696 |
| Flow | 5.0E-5 - 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow | 4.0E-5 - 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.0E-5 - 5.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.9E-5 - 5.6E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| 23°C | 0.22 - 0.23 | W/m/K | ASTM C177 |
| 23°C | 0.21 - 0.26 | W/m/K | ISO 8302 |
| RTI Elec | 169 - 171 | °C | UL 746 |
| RTI Imp | 169 - 171 | °C | UL 746 |
| RTI | 169 - 171 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 4.0E+15 | ohms | ASTM D257 |
| -- | 5.1E+5 - 1.7E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 10 - 1.0E+17 | ohms·cm | ASTM D257 |
| 23°C | 5.1E+5 - 3.3E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 14 - 34 | kV/mm | ASTM D149 |
| 23°C | 16 - 33 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.15 - 3.43 | ASTM D150 | |
| 23°C | 2.90 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 1.0E-3 - 7.6E-3 | ASTM D150 | |
| 23°C | 5.0E-4 - 0.025 | IEC 60250 | |
| Comparative Tracking Index | 100 - 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | |||
| -- | 44 - 48 | % | ASTM D2863 |
| -- | 45 - 47 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 134 - 150 | °C | |
| Drying Time | 5.0 - 5.1 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Hopper Temperature | 89.5 - 100 | °C | |
| Rear Temperature | 338 - 372 | °C | |
| Middle Temperature | 364 - 383 | °C | |
| Front Temperature | 370 - 395 | °C | |
| Nozzle Temperature | 370 - 388 | °C | |
| Processing (Melt) Temp | 373 - 393 | °C | |
| Mold Temperature | 148 - 150 | °C | |
| Injection Pressure | 103 - 104 | MPa | |
| Back Pressure | 0.506 - 0.521 | MPa | |
| Screw Speed | 55 - 56 | rpm | |
| Vent Depth | 0.051 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEIThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 144 | °C | |
| Drying Time | 5.0 - 5.1 | hr | |
| Suggested Max Moisture | 0.015 - 0.020 | % | |
| Hopper Temperature | 89.8 - 90.0 | °C | |
| Cylinder Zone 1 Temp. | 270 - 336 | °C | |
| Cylinder Zone 2 Temp. | 288 - 343 | °C | |
| Cylinder Zone 3 Temp. | 298 - 343 | °C | |
| Cylinder Zone 4 Temp. | 303 - 343 | °C | |
| Adapter Temperature | 290 - 343 | °C | |
| Melt Temperature | 295 - 324 | °C | |
| Die Temperature | 285 - 342 | °C | |
| Calibration Temp, First | 144 - 155 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEIThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 TFE 10 HB | RTP Company | ABS | RTP |
| 4LAC® 25H20400 AS | 4Plas | ABS | 4LAC® |
| Nypol® PA B3 G5 BRC0001 NT312 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| KOPELEN JM-380UN | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| MAJORIS GFRH300 BLACK 8229 | AD majoris | PP, Unspecified | MAJORIS |