Makroblend® EC5005 HT
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | prMaoU_MakroblendEC5005HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+PBT)-Blend; impact modified; injection molding; flame-retardant; relative temperature index =100°C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Transverse flow 1 | 0.60 - 0.80 | % | ISO 2577 |
| Lateral flow : 90°C, 1 hour | 0.10 - 0.20 | % | ISO 2577 |
| Flow 2 | 0.60 - 0.80 | % | ISO 2577 |
| Traffic : 90°C, 1 hour | 0.10 - 0.20 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.36 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 65.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 48.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield, 23°C | 3.6 | % | ISO 527-2/5 |
| Fracture, 23°C | 12 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 3(23°C) | 3600 | MPa | ISO 178 |
| Flexural Stress 4(3.5% Strain, 23°C) | 100 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 5(23°C) | 4.7 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Combustion rate- US-FMVSS (> 1.00 mm) | passed | ISO 3795 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 85 | kJ/m² | ISO 179/1eU |
| 23°C | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 50 | kJ/m² | ISO 180/1C |
| -20°C | 5.0 | kJ/m² | ISO 180/A |
| 23°C | 5.0 | kJ/m² | ISO 180/A |
| 23°C | 55 | kJ/m² | ISO 180/1C |
| Multi-Axial Instrumented Impact Energy (23°C) | 25.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 3600 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 91.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 100 | °C | UL 746 |
| RTI | 100 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 32 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.30 | IEC 60250 | |
| 23°C, 1 MHz | 3.20 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.3E-3 | IEC 60250 | |
| 23°C, 1 MHz | 0.014 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 3.0 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.5 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.5 mm) | 700 | °C | IEC 60695-2-13 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1000 sec^-1) | 340 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 600 bar |
| 2 . | 600 bar |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 20 TFE 15 | RTP Company | Nylon 66 | RTP |
| Chiao Fu PBT PBT312G30 BK | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Elvax® 760 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Hiprolon® 70 NN LM | Arkema | Nylon 610 | Hiprolon® |
| Sumiliteresin® PR-8000 | SBHPP | Phenolic | Sumiliteresin® |