ULTEM™ 1000P resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | prFaGx_ULTEM1000Presin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard flow Polyetherimide (Tg 217C) in 350 micron powder. ECO Conforming. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3590 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3310 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 152 | MPa | ASTM D790 |
| Poisson's Ratio | 0.36 | ASTM D638 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 36.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 210 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 201 | °C | ASTM D648 |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -20 to 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 33 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.15 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.3E-3 | ASTM D150 | |
| 2.45 GHz | 2.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 47 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 4104 | Prime PVC® | PVC, Rigid | Prime |
| SINOF P265U | SINOF HI-TECH MATERIAL CO. LTD | PPS | SINOF |
| VENYL SFRHG309 - 8229 | AD majoris | Nylon 6 | VENYL |
| Jampilen HP528H | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Sylvin 9302-70 FU White 1327 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |