Starpylen HU 70E3
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pq9KQN_Starpylen-HU-70E3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen HU 70E3 is a High Density Polypropylene Injection Molding Resin (also know as HU70E3) |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.91 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.80 to 1.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 18.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 25 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3000 | MPa | ISO 178 |
| Flexural Stress | 33.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 64.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV X17175B | Teknor Apex Company | TPV | Sarlink® TPV |
| Vydyne® R413 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| 4TECH® 9B20000 E-S | 4Plas | Nylon 6 | 4TECH® |
| Latiohm 73-09 PD01 G/20 | LATI S.p.A. | Acetal (POM) Copolymer | Latiohm |
| Optema™ TC 110 Molding | ExxonMobil Chemical | EMA | Optema™ |