DOWLEX™ 2342M
| Category: | HDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ppxPqd_DOWLEX-2342M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2342M Polyethylene Resin is a high density ethylene/octene copolymer resin. It has a unique molecular structure with a linear polyethylene backbone and controlled octene side branches, which provides a combination of flexibility with very high toughness and stress crack resistance. A specified carbon black masterbatch is incorporated into the DOWLEX 2342M Polyethylene Resin during extrusion to arrive at a fully stabilised, homogeneous black sheet with excellent weldability. Sheeting thus produced meets the requirements of the Guidelines and Directives controlling general water barrier membranes such as the North Rhine Westfalia Guidelines or "Guideline for Plastic Membranes in Landfill sites" issued 7/92 from B.A.M. Berlin. Processability: Typical extrusion temperature range for DOWLEX 2342M Polyethylene Resin is 190 to 230 °C. The resin contains processing stabilisers compatible with those in the Masterbatch added to guarantee short and long term processing, thermal and environmental stability including metal deactivators. Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ISO 1183 | ||
| -- 1 | 0.944 | g/cm³ | |
| -- | 0.932 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.85 | g/10 min | |
| 190°C/5.0 kg | 2.6 | g/10 min | |
| Environmental Stress-Cracking Resistance (20°C, 2.00 mm, 10% Antarox, Compression Molded) | > 15000 | hr | ASTM D1693A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 2.00 mm, Compression Molded) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield 2 | 18.0 | MPa | ISO 527-2 |
| Yield, 2.00 mm, Compression Molded 3 | 16.0 | MPa | ISO 527-2/50 |
| Break 4 | > 30.0 | MPa | ISO 527-2 |
| Break, 2.00 mm, Compression Molded 5 | > 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield 6 | 12 | % | ISO 527-2 |
| Yield, 2.00 mm, Compression Molded 7 | 14 | % | ISO 527-2/50 |
| Break 8 | > 800 | % | ISO 527-2 |
| Break, 2.00 mm, Compression Molded 9 | > 800 | % | ISO 527-2/50 |
| Flexural Modulus - 2% Secant (2.00 mm, Compression Molded) | 550 | MPa | ISO 178 |
| Tear Resistance 10 | > 750 | N | DIN 53356 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | > 30 | min | DIN EN 728 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Force 11 | > 7500 | N | DIN 54307 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 12 | ISO 180 | ||
| -40°C, Compression Molded | 65 | kJ/m² | |
| 23°C, Compression Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 117 | °C | ISO 306/A120 |
| Note Message | |
|---|---|
| 1 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 2 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 3 . | Data are valid for MD and CD direction. |
| 4 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 5 . | Data are valid for MD and CD direction. |
| 6 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 7 . | Data are valid for MD and CD direction. |
| 8 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 9 . | Data are valid for MD and CD direction. |
| 10 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 11 . | Black 2.5 mm thick sheet extruded from DOWLEX 2342M Polyethylene resin with a specified masterbatch conforming to DIN 16776 as: "PE, EACK 35T022 or D006". Carbon black content: 2.0-2.2%. |
| 12 . | 2 mm thick |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SAP-6318XB35 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| Sindustris ABS LRS911D | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TEREZ PA 6 7400 GK 50 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Unichem 1077 | Colorite Polymers | PVC, Flexible | Unichem |
| OpteSTAT™ PA6,6 DP502 | Ovation Polymers Inc. | Nylon 66 | OpteSTAT™ |