Genestar™ G1301A-M61
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Genestar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ppefRG_Genestar-G1301A-M61.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Genestar G1301A-M61 is a 30% glass reinforced and impact modified injection grade. Main feature of G1301A-M61 are;
Examples of application are;
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.30 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ISO 178 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Coefficient of Friction 1 | 0.30 | JIS K7218 | |
| Abrasion Loss 2 | 15.0 | mg | JIS K7218 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 17 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | °C | ISO 75-2/Af |
| Glass Transition Temperature | 125 | °C | |
| Melting Temperature | 300 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Critical PV value : 1000 kg/cm²*cm/sec (JIS K7218-A) |
| Note Message | |
|---|---|
| 1 . | P=10kgf/cm² |
| 2 . | P=10kgf/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 4017 UV2 | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
| DINALON® PA 6 ESPECIAL IMPACTO | Grupo Repol | Nylon 6 | DINALON® |
| Globalprene® 3501W | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Deprene 201-87 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| POCAN® KU 1-7635 POS 151 000000 | LANXESS GmbH | PC+PBT | POCAN® |