MAJORIS BW300 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pmnlXE_MAJORIS-BW300---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BW300 - 8229 is a 30% glass - filled polypropylene compound intended for injection moulding. The product is available in both black (BW300 - 8229) and natural (BW300) but other colours can be provided on request. BW300 - 8229 has been developed especially for the automotive applications and electrical components. The good flowability of BW300 - 8229 makes it very easy to process even for complicated parts with long flow paths and it offers very high productivity with short cycle times. BW300 - 8229 is formulated to give an excellent surface finish with good scuff resistance. APPLICATIONS Products requiring good rigidity, low shrinkage, high dimensional stability can suitably be made from BW300 - 8229. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 24 | % | ISO 527-2 |
| Flexural Modulus 1 | 2050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 64.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 8300 | Formosa Plastics Corporation | HDPE | TAISOX |
| Moplen T30SW | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| LEXAN™ EM1210 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| POLYFORT® 140-3020 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Elastocon® 2855 | Elastocon TPE Technologies | TPE | Elastocon® |