Sumikon® FM-TK210
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sumitomo Bakelite Co., Ltd. |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pmgSUc_Sumikon-FM-TK210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This molding compound posses about 10 to 100 times higher thermal conductivity than conventional plastics. This compound has widened the range of applications to parts which could not previously be made of plastic because of heat accumulation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.83 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.40 | % | ASTM D638 |
| Flexural Modulus | 21000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 132 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Thermal Conductivity | 7.0 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Mold Temperature | 120 - 150 | °C |
| Injection instructions |
|---|
| Cylinder temperature: 290 to 340°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 60A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Starex VH-0800 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| TEREZ PA 6.6 HT 8500 GF 50 HY | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Globalene® 7011 | Lee Chang Yung Chemical Industry Corp. | PP Impact Copolymer | Globalene® |
| Deprene 251-70 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |