Ingeo™ 6100D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | plswIw_Ingeo-6100D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ingeo biopolymer 6100D, a NatureWorks product, is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6100D is designed for extrusion into mechanically drawn staple fibers or continuous filament, using conventional fiber spinning and drawing equipment. 6100D is typically well suited for fiber processes where lower fiber shrinkage and higher dimensional stability is required. Ingeo biopolymer 6100D can be converted into a broad range of fiber products. Potential applications for Ingeo biopolymer 6100D include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| Relative Viscosity 1 | 3.1 | ASTM D5225 | |
| Shrinkage | ASTM D2102 | ||
| Boiling Water | 3.0 - 10 | % | ASTM D2102 |
| Hot Air : 130°C 2 | 3.0 - 10 | % | ASTM D2102 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| modulus of elasticity | 55.0 - 65.0 | g/denier | ASTM D2256 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Denier - per filament 3 | > 0.500 | ||
| Elongation of Fibers | 10 - 70 | % | ASTM D2256 |
| Tenacity of Fibers | 3.00 - 6.00 | g/denier | ASTM D2256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 - 60.0 | °C | ASTM D3417 |
| Peak Crystallization Temperature (DSC) | 165 - 180 | °C | ASTM D3418 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density (230°C) | 1.08 | g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | < 5.0E-3 | % | |
| Melt Temperature | 220 - 240 | °C |
| Extrusion instructions |
|---|
| General-purpose screws with L/D ratios of 24:1 to 30:1 and 3:1 compression ratios are recommended. |
| Note Message | |
|---|---|
| 1 . | Measured at 1.0 g/dL in chloroform at 30°C |
| 2 . | 10 min |
| 3 . | g/9000m |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 1210 TF HS UV3 | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| Sylvin 8472-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CERTENE™ 705 SAN | Muehlstein | SAN | CERTENE™ |
| KOPLA PC KTE1707 | KOPLA Co., Ltd. | PC+PBT | KOPLA PC |
| LG PVC PB1302 | LG Chem Ltd. | PVC Copolymer | LG PVC |