POLYLAC® PA-756H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pktWrG_POLYLAC-PA-756H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-756H is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 8.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 75 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 12.7 mm) | 115 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 107 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 3.18 mm 1 | 39.2 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break, 3.18 mm 2 | 10 | % | ASTM D638 |
| Break | 35 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.35 mm 3 | 2260 | MPa | ASTM D790 |
| -- 4 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 5 | 62.8 | MPa | ASTM D790 |
| -- 6 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 100 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 90 | J/m | ASTM D256 |
| -- | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 50 | kJ/m² | ISO 180/1U |
| Impact Flexural Test | |||
| Notched | 8.00 | kJ/m² | ISO 179/2C |
| Unnotched | 110 | kJ/m² | ISO 179/2D |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.35 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 89.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525 7 |
| -- | 102 | °C | ISO 306/A50 |
| -- | 104 | °C | ISO 306/A120 |
| -- | 95.0 | °C | ISO 306/B50 |
| -- | 97.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | HB | ||
| 1.59 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 190 to 230 | °C | |
| Front Temperature | 190 to 230 | °C | |
| Nozzle Temperature | 190 to 230 | °C | |
| Mold Temperature | 30.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® E-1822-PL 31 | Unipack Plasindo | PVC, Unspecified | polyvic® |
| Purell HP548N | LyondellBasell Industries | PP Homopolymer | Purell |
| KumhoSunny PC/PBT HCB9320G | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PBT | KumhoSunny PC/PBT |
| MAJORIS AT200 | AD majoris | PP, Unspecified | MAJORIS |
| OmniLon™ PA6/6 GR33 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |