LNP™ LUBRICOMP™ Cycoloy_C6303 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pkdlpt_LNP-LUBRICOMP-Cycoloy-C6303-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP CYCOLOY_C6303 compound is a Wear resistant (5% PTFE), flame retardant PC+ABS. High heat and good hydrolytic stability. UL listing from Japan and Pacific. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 260°C/2.16 kg | 10 | g/10 min | |
| 260°C/5.0 kg | 50 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2690 | MPa | ASTM D638 |
| -- | 2870 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.5 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2/5 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break 3 | 51.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.5 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Yield | 4.6 | % | ISO 527-2/50 |
| Break 5 | 30 | % | ASTM D638 |
| Break | 22 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2760 | MPa | ASTM D790 |
| -- 7 | 2600 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 9 | 7.4 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 48.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 109 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 92.8 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 102 | °C | |
| Vicat Softening Temperature | |||
| -- | 118 | °C | ASTM D1525 10 |
| -- | 117 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.19 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 2.49 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 221 to 266 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Nozzle Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 243 to 277 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3571EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| Mecoline S RDX 1215 F | Melos GmbH | TP, Unspecified | Mecoline |
| Monprene® WR-12233 | Teknor Apex Company | TPE | Monprene® |
| ECONAMID® 6G30FL | DOMO Engineering Plastics SPA | Nylon 6 | ECONAMID® |
| HiFill® PA6/6 GF10 IM L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |