Synthos EPS® 0513F/CZ
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos EPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pkASi5_Synthos-EPS-0513F-CZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Synthos EPS®/CZ types 0513F, 0814F, 0822F, 1020F, 1640F i 2040F are self-extinguishing expandable polystyrene EPS with high content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. Synthos EPS® 0513F/CZ (Koplen 0513F) is mainly used for production of shaped parts with wall thickness above 10 mm (e.g. shipping packaging for glass and electrical goods, building bricks, floor and roof shaped parts); production of smaller blocks with higher density or cutted profiles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density 1 | 0.02 to 0.04 | g/cm³ | Internal Method |
| Moisture Content | < 10000 | ppm | Internal Method |
| Particle Size - >95% between | 500 to 1000 | µm | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Reaction to Fire | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 7.0 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2819-80 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| HFFR 2005PC | Teknor Apex Company | Polyolefin, Unspecified | HFFR |
| Hostacom 515-UV | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| MAJORIS GE460 - 6744 | AD majoris | PP, Unspecified | MAJORIS |
| Durethan® AKV 50 000000 | LANXESS GmbH | Nylon 66 | Durethan® |