TRANSMARE® BIO 35LA-0.001
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pk8A1G_TRANSMARE-BIO-35LA-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® BIO 35LA-0.001 is a PLA INGEO™ based biopolymer with good flow. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 35 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 81 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 3420 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 72.0 | MPa | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 2.8 | % | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus (Injection Molded) | 3460 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | < 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C, injection molding | 1.6 | kJ/m² | ISO 179/1A |
| 0°C, injection molding | 1.6 | kJ/m² | ISO 179/1A |
| 23°C, injection molding | 1.5 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C, injection molding | 25 | kJ/m² | ISO 179/1U |
| 23°C, injection molding | 18 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C, Injection Molded) | 2.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C, Injection Molded) | 16 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 51.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 62.5 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 25.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 6261-H/G | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| BLUESTAR® PBT 201-G30202 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| BMC 3001F | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Petrothene® GA616050 | LyondellBasell Industries | LLDPE | Petrothene® |
| Sylvin 916VO-95C White 1441 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |