Ingeo™ 6204D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | phgD6E_Ingeo-6204D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureWorks® PLA polymer 6204D, a NatureWorks LLC product, is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6204D is designed for extrusion into mechanically drawn staple fibers or continuous filament, using conventional fiber spinning and drawing equipment. 6204D is typically well suited for fiber processes where deeper disperse dying in the final product is desired: partially orientated yarn (POY), fully drawn yarn (FDY), staple fibers, and continuous filament. NatureWorks® PLA 6204 can be converted into a broad range of fiber products. Potential applications for PLA polymer 6204D include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 15 to 30 | g/10 min | ASTM D1238 |
| Relative Viscosity | 3.10 | Internal Method | |
| Shrinkage | ASTM D2102 | ||
| Boiling Water | 5.0 to 15 | % | |
| Hot Air : 130°C 1 | 5.0 to 15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Modulus of Elasticity | 30.0 to 40.0 | g/denier | ASTM D2256 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Denier - per filament | > 0.500 | ||
| Elongation of Fibers | 10 to 70 | % | ASTM D2256 |
| Tenacity of Fibers | 2.50 to 5.00 | g/denier | ASTM D2256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 to 60.0 | °C | ASTM D3417 |
| Peak Crystallization Temperature (DSC) | 155 to 170 | °C | ASTM D3418 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density (230°C) | 1.08 | g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 5.0E-3 | % | |
| Melt Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | 10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRALOY 805 / C01000 natur | SITRAPLAS GmbH | PC+ABS | SITRALOY |
| Gallonprene® GP100-2501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Electroblend® PP-1800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Homopolymer | Electroblend® |
| ISPLEN® PP 086 U6E | REPSOL | PP Homopolymer | ISPLEN® |
| PERSTIR® N09K7000AE0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |