POCAN® S 7926 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | phRt1P_POCANS7926000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding, extrusion, flame retardant, improved impact strength |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.37 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (270°C/5.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 250°C, 2.00mm 1 | 2.0 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.30 | % | ISO 2577 |
| Flow direction : 250°C, 2.00mm 3 | 2.1 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.30 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 10 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2300 | MPa | ISO 899-1 |
| 1000 hr | 1500 | MPa | ISO 899-1 |
| Flexural Modulus 5(23°C) | 2300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 65.0 | MPa | ISO 178/A |
| 23°C 6 | 70.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength (23°C) 7 | 5.0 | % | ISO 178/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| Electric Strength | 13.0 | °C | IEC 60216 |
| Tensile Impact Strength | 5.5 | °C | IEC 60216 |
| Tensile Strength | 13.0 | °C | IEC 60216 |
| Temperature index | IEC 60216 | ||
| Electric Strength, 20000 hr | 140 | °C | IEC 60216 |
| Tensile Impact Strength, 20000 hr | 110 | °C | IEC 60216 |
| Tensile Strength, 20000 hr | 140 | °C | IEC 60216 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GFHMPR, 11-020 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 110 | kJ/m² | ISO 180/1U |
| 23°C | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Energy (23°C, Energy to Peak Force) | 80.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 47.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 160 | °C | ISO 306/B120 |
| Ball Pressure Test (190°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.25 | W/m/K | ISO 8302 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | IEC 60250 | |
| 23°C, 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.5E-3 | IEC 60250 | |
| 23°C, 1 MHz | 0.015 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 700 | °C | IEC 60695-2-13 |
| 1.60 mm | 700 | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® P 80 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| 4MID® 9A24100 | 4Plas | Nylon 66 | 4MID® |
| Lumid® GP2200A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| MAJORIS G400WA | AD majoris | PP, Unspecified | MAJORIS |
| Pebax® 3533 SN 01 | Arkema | PEBA-Ether | Pebax® |