Celanex® 3216
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | phRb7T_Celanex-3216.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3216 is a non-exuding (UL and CSA approved V-0 at 1/32 inch and 5V at 1/8 inch ), 15% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties and processability. It is well suited for electrical connector applications where its UL approved 50% regrind use capability allows maximum use of purchased product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.60 | % | ASTM D955 |
| Vertical flow direction | 1.1 | % | ISO 294-4 |
| Flow direction | 0.30 - 0.60 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.17 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 87 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 100 | MPa | ASTM D638 |
| Fracture | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 4.0 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 28 | kJ/m² | ISO 179/1eU |
| 23°C | 28 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 217 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 185 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 95.0 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 206 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 2.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 26 | kV/mm | ASTM D149 |
| -- | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| 100 Hz | 3.70 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.010 | ASTM D150 | |
| 100 Hz | 3.3E-3 | IEC 60250 | |
| 1 MHz | 0.016 | IEC 60250 | |
| Arc Resistance | 79.0 | sec | ASTM D495 |
| Comparative Tracking Index | 250 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Oxygen Index | 27 - 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 50 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 255 | °C | |
| Processing (Melt) Temp | 235 - 255 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 255°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Impact Copolymer CP410 | M. Holland Company | PP Impact Copolymer | MTEGRITY™ PP Impact Copolymer |
| VESTAMID® Terra DS18 natural color | Evonik Industries AG | Nylon 1010 | VESTAMID® Terra |
| Andur 2-920 AP | Anderson Development Company | PUR-Est/eth,TDI | Andur |
| Magnobond 95 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| LNP™ LUBRICOMP™ WBL36L compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |