Quadrant EPP Nylatron® MC® 907
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | phQCiY_Quadrant-EPP-Nylatron-MC-907.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Nylatron® MC® 907 is a Polyamide 6 (Nylon 6) product. It can be processed by casting and is available in North America. Typical application: Food Contact Applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.60 | % | |
| Saturation | 7.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 85 | ||
| R-Scale | 115 | ||
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 110 | MPa | ASTM D790 |
| Compressive Modulus | 2760 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 103 | MPa | ASTM D695 |
| Shear Strength | 75.8 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.20 | Internal Method | |
| Wear Factor | 200 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 93 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.105 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 216 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7868-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wellamid® MRGF25/15 42H-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Cri-Line TFEP-820 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Lionpol HF-203552 | Lion Polymers Incorporated | TPE | Lionpol |
| MACOMASS PP MM-PP HG 23 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |