Vydyne® 22HSP NT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ph6mS8_Vydyne-22HSP-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vydyne 22HSP NT product description to come. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 2.0 | -- | % | |
| Flow : 23°C, 2.00 mm | 2.2 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | 1800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 85.0 | 55.0 | MPa | |
| Break, 23°C | 55.0 | 40.0 | MPa | |
| Tensile Strain (Yield, 23°C) | 5.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2900 | 1000 | MPa | ISO 178 |
| Flexural Strength (23°C) | 95.0 | 30.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 7.0 | kJ/m² | |
| 23°C | 6.0 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 5.0 | 7.0 | kJ/m² | |
| 23°C | 6.0 | 20 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.710 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 110 | -- | °C | |
| 3.00 mm | 110 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 115 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 400 to 599 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.710 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.710 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 4 | -- | ||
| 3.00 mm | PLC 4 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.710 mm | 825 | -- | °C | |
| 1.50 mm | 825 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.710 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 70.0 | °C | |
| Drying Time | 1.0 to 3.0 | hr | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 285 to 300 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVERLON® TM-45GWX | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| Fainplast PVC PH 82/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Ferro PP TPP40AE56AL ALMOND | Ferro Corporation | PP Homopolymer | Ferro PP |
| DOMAMID® 6AVUV | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| POLYFLAM® RIPP 490 E CS1 | A. Schulman Europe | PP Copolymer | POLYFLAM® |