EPO-TEK® 930-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pgtWyg_EPO-TEK-930-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two part, thermally conductive, electrically insulating epoxy. It can be used for heat sinking semiconductor devices, hybrid microelectronics, optics or medical devices. It is a lower viscosity and smaller particle size alternative to EPO-TEK® 930. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 415 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 5.47 | GPa | |
| Thixotropic Index | 3.80 | ||
| Weight Loss on Heating | |||
| 200°C | 0.090 | % | |
| 250°C | 0.50 | % | |
| 300°C | 1.3 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 70.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.8E-5 | cm/cm/°C | |
| -- 3 | 9.6E-5 | cm/cm/°C | |
| Thermal Conductivity | 1.1 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 4.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | White | ||
| Density | |||
| Part B | 1.03 | g/cm³ | |
| Part A | 1.40 | g/cm³ | |
| Viscosity 6(23°C) | 60 to 80 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 1400 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 | ||
| Lap Shear Strength (23°C) | 11.3 | MPa | |
| Relative Permittivity (1 kHz) | 3.99 | ||
| Volume Resistivity (23°C) | > 1.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 4.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 5 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 7 T 13 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| AEI SX538:CM540U | AEI Compounds Limited | XLPE | AEI |
| APEX® 1001 | Teknor Apex Company | PVC, Flexible | APEX® |
| POLYFLON™ F-208 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7502BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |