PALFORM® R H 50 Datasheet,Acetal (POM) Homopolymer,pal plast GmbH-SHANGHAI SUSHENG

Message
PALFORM®R H 50 is a polyoxymethylene (POM) homopolymer product,. It can be processed by injection molding and is available in Europe. Typical application areas are: engineering/industrial accessories. Features include: flame retardant/rated flame chemical resistance high strength Impact resistance Medium viscosity

General Information
Features	High strength Impact resistance, high Good chemical resistance Fuel resistance Medium viscosity
Uses	Gear Bearing
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)	13.5	cm³/10min	ISO 1133
Water Absorption			ISO 62
Saturated, 23°C	0.80	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3100	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	70.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	14	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	28	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	159	°C	ISO 306/B50
Melting Temperature (DSC)	178	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 190°C/2.16 kg: 12 to 15 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3000 to 3200 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 68 to 72 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 12 to 15 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 25 to 30 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 7 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 157 to 160 °CDensity, ISO 1183: 1.4 to 1.42 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.7 to 0.9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 190°C/2.16 kg: 12 to 15 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3000 to 3200 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 68 to 72 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 12 to 15 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 25 to 30 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 7 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 157 to 160 °CDensity, ISO 1183: 1.4 to 1.42 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.7 to 0.9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Category:	Acetal (POM) Homopolymer , Acetal (POM) Homopolymer
Manufacturer:	pal plast GmbH
Trademark:	PALFORM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pftn6M_PALFORM-R-H-50.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Star L PA6 30V D31	Eurostar Engineering Plastics	Nylon 6	Star L
NuSil CF2-3521-2	NuSil Technology	Silicone	NuSil
LEXAN™ LUX9132C resin	SABIC Innovative Plastics	PC	LEXAN™
LGH 304	LG Polymers India Pvt. Ltd.	PS (HIPS)	LGH
Lytex 9063	Quantum Composites Inc.	Epoxy	Lytex