LEXAN™ LUX9230T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pfZtM6_LEXAN-LUX9230T-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUX9230T Polycarbonate (PC) resin is a non-filled, UV within, injection moldable grade. This halogen-free flame retardant PC has a V0 UL rating and melt flow rate (MFR) of 14. It is intended to meet with all environmental labels and requirements. LUX9230T is available in transparent and tinted color options and is a general-purpose resin potentially for a wide variety of applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2280 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.1 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 3 | 67.6 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 130 | % | ASTM D638 |
| Break | 85 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2150 | MPa | ASTM D790 |
| -- 7 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D256 |
| 23°C 9 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 79.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 10 | 124 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525 11 |
| -- | 141 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 | ||
| Arc Resistance 12 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 3.05 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 120*10*4 mm |
| 11 . | Rate B (120°C/h), Loading 2 (50 N) |
| 12 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 228 | Mitsubishi Chemical Performance Polymers, Inc. | SEBS | tefabloc® |
| ALFATER XL® D40E 1GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| BMC 501 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| API PS 505 HF | American Polymers, Inc. | PS (MIPS) | API PS |
| PERSTIR® B43K7000AH0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |