ENVIRON® ENV39-NC430
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIRON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pfWzeH_ENVIRON-ENV39-NC430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, UV Stabilized, w/Mold Release, Low Temperature Impact and Chemical Resistance, Automotive Exterior and OVAD Applications, RoHS Compliant NC430 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 59.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 90.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 210 | J/m | |
| 23°C | 680 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.6 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 254 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-765A | CHI MEI CORPORATION | ABS | POLYLAC® |
| ALAMID® 6.6 GK 50 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| AMPLIFY™ TY 1053H | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| Petlon R-Prime N3-00-65-BK | Petlon Polymers Ltd | PC+ABS | Petlon R-Prime |