NORYL GTX™ GTX810 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pehRFv_NORYLGTXGTX810resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX810 is a 10% glass reinforced grade with excellent chemical resistance in combination with high stiffness and high heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.60 - 1.0 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 65.0 | MPa | ISO 527-2/5 |
| Fracture | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.5 | % | ISO 527-2/5 |
| Fracture | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 2900 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -20°C | 4.0 | kJ/m² | ISO 179/2C |
| 23°C | 6.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 200 | °C | ISO 306/B50 |
| -- | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene MDPE 3802 (Wire and Cable) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Fiberfil® J-60/30 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| DuPure® SM 76 A | Ducor Petrochemicals BV | PP Impact Copolymer | DuPure® |
| KOCETAL® GF702WH | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| INELEC TPUCF1050D | Infinity LTL Engineered Compounds | TPU, Unspecified | INELEC |