NuSil MED-4165

Category:	Rubber , Rubber
Manufacturer:	NuSil Technology
Trademark:	NuSil
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ped36E_NuSil-MED-4165.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: UNCATALYZED

Message

NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications.

HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus.

HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts.

Comments: UNCATALYZED

General Information
Uses	Washer Pipe fittings Balloon application Profile Medical/nursing supplies
Agency Ratings	USP Class VI
Processing Method	Extrusion Resin transfer molding Profile extrusion molding Compression molding Calendering

Mechanical	Nominal Value	Unit
Tensile Strength (200% Strain)	3.10	MPa

Thermoset	Nominal Value	Unit
Post Cure Time (177°C)	2.0	hr

Additional Information	Nominal Value	Unit
Cure System	Peroxide
Plasticity: 115 mils

Uncured Properties	Nominal Value	Unit
Density	1.21	g/cm³
Curing Time (116°C)	0.083	hr

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	65
Tensile Strength	8.27	MPa
Tensile Elongation at Break	500	%
Tear Strength	35.0	kN/m

Resin Grade	Manufacturer	Category	Trademark
Shuang-Bang AB-122A	Shuang-Bang Industrial Corp.	PUR, Unspecified	Shuang-Bang
Sinkral® PD D 232/M4	Versalis S.p.A.	ABS	Sinkral®
Tenogel® ABS A3 HS NTLA013 AB329	Petropol Industry and Trade of Polymers LTDA	ABS	Tenogel® ABS
POLYFLON™ D-210C	Daikin Fluorochemicals (China) Co., Ltd.	PTFE	POLYFLON™
Sylvin 9925-70UV Grey 9526	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin