REPRO PP R610
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Rondo Plast AB |
| Trademark: | REPRO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | peOEZr_REPRO-PP-R610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection moulding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow | 1.2 to 1.6 | % | |
| Flow | 1.2 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1100 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 40.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 to 2.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1307 UP | RTP Company | PPS | RTP |
| StarMediflex P 7025-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| Karina BLACK PVC COMP. -E700-48/ I-J-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| FUDOWLITE® F900 | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |
| LNP™ THERMOCOMP™ WF008 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |