MAJORIS EB669
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pdgAo5_MAJORIS-EB669.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EB669 is a natural, 65% mineral filled polypropylene compound intended for injection moulding. The product is available in natural (EB669) but other colours can be supplied on request. EB669 has been developed for applications where high density, good impact strength, good surface finish and good flow properties are necessary. APPLICATIONS High density products, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.87 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1530 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2850 | MPa | ISO 178 |
| Flexural Stress | 43.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 23 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 134 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 77.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HR980UE | LyondellBasell Industries | PP, Unspecified | Supol |
| Wellamid® 22LHI4 XE-GY1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| KMI PP KM-003IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Hostacom EP3307 C12360 | LyondellBasell Industries | PP Copolymer | Hostacom |
| ULTEM™ AUT230 resin | SABIC Innovative Plastics | PEI | ULTEM™ |