Ultramid® 1503-2 BK ND3007
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pddc4d_Ultramid-1503-2-BK-ND3007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.7 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10800 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 190 | 144 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 9900 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 264 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.040 to 0.20 | % | |
| Processing (Melt) Temp | 288 to 305 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 40 to 80 | rpm | |
| Screw Compression Ratio | 3.0:1.0 to 4.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 660.5 FR | RTP Company | ABS | RTP |
| Torlon® 4645 | Solvay Specialty Polymers | PAI | Torlon® |
| apilon 52® D1 58L | API SpA | TPU-Polyester | apilon 52® |
| Karina BEIGE PVC COMPOUND 900-08/16-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMP -E 754-10/425-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |