MEGOLON™ S540E
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pcwMLw_MEGOLON-S540E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MEGOLON® S540E is a thermoplastic, halogen free cable sheathing compound which exhibits an excellent level of fire retardancy. This product is specifically aimed at designs of cables requiring a good degree of flexibility and the ability to meet the more stringent fire test specifications. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 1 | 14.2 | MPa | IEC 60811-1-2 |
| -- | 11.5 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Break 2 | 140 | % | IEC 60811-1-2 |
| Break | 200 | % | IEC 60811-1-1 |
| Elongation at Break | |||
| after 4 hours, in IRM 902 Oil : 70°C | 250 | % | |
| after 7 days, in IRM 902 Oil : 23°C | 220 | % | |
| after 7 days, in IRM 903 Oil : 23°C | 160 | % | |
| Tensile Strength | |||
| after 4 hours, in IRM 902 Oil : 70°C | 9.20 | MPa | |
| after 7 days, in IRM 902 Oil : 23°C | 12.0 | MPa | |
| after 7 days, in IRM 903 Oil : 23°C | 7.50 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test (80°C) | 35 | % | IEC 60811-3-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission Conductivity | 7.50 | µS/cm | IEC 60754-2 |
| Acid Gas Emission pH | 5.50 | IEC 60754-2 | |
| Flammability Temperature Index | 330 | °C | ISO 4589-3 |
| Smoke Density | ASTM E662 | ||
| Flaming mode 3 | < 90 | Ds | |
| Non-flaming mode 4 | < 200 | Ds | |
| Toxicity | 0.400 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | 0.0 | % | IEC 60754-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | 23 | % | |
| Change in Tensile Strain at Break in Air (100°C, 168 hr) | -30 | % | |
| Change in Tensile Stress | |||
| 23°C, 168 hr, in IRM 902 Oil | 5.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -35 | % | |
| 70°C, 4 hr, in IRM 902 Oil | -20 | % | |
| Change in Tensile Strain at Break | |||
| 23°C, 168 hr, in IRM 902 Oil | 10 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -20 | % | |
| 70°C, 4 hr, in IRM 902 Oil | 25 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 45 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | after 7 days at 100°C |
| 2 . | after 7 days at 100°C |
| 3 . | Time to maximum: 12 minutes |
| 4 . | Time to maximum: 13 minutes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2990-75 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Andur 2-92 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| DuraFlex 828 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| Hostacom X M3 T15 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| PPR 6605HI | Premier Plastic Resins, Inc. | Nylon 66 | PPR |