LNP™ LUBRICOMP™ OX88533 compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pcWzyS_LNP-LUBRICOMP-OX88533-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OX88533 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-O-88533 Product reorder name: OX88533 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.53 | % | ISO 294-4 |
| Flow : 24 hr | 0.090 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13100 | MPa | ASTM D638 |
| -- | 12200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 145 | MPa | ASTM D638 |
| Break | 146 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 11000 | MPa | ASTM D790 |
| -- | 11400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 209 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.43 | ||
| vs. Itself - Static | 0.34 | ||
| Wear Factor - Washer | 59.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 9.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D4812 |
| 23°C 3 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.20 | J | ASTM D3763 |
| -- | 3.07 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 264 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 260 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1050-OR3-LF | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Kingfa PP-R009 | Kingfa | PP, Unspecified | Kingfa |
| PERCOM® XG1128/2 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| MTEGRITY™ LLDPE LL104AH | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |
| Tunhe PBT TH6080 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |