Crastin® T843FR NC010

Category:	PBT , THERMOPLASTIC POLYESTER RESIN
Manufacturer:	DuPont Performance Polymers
Trademark:	Crastin®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pcERvv_CrastinT843FRNC010.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
20% Glass Reinforced, Toughened, Flame Retardant, Polybutylene Terephthalate with Improved Impact Resistance

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Additive	demoulding Flame retardancy
Features	Impact resistance, good Flame retardancy
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Sheet extrusion molding Profile extrusion molding Injection molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>PBTC-GF20FR(17)
Resin ID (ISO 1043)	PBTC-GF20FR(17)

Physical	Nominal Value	Unit	Test Method
Density	1.60	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)	10.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Transverse flow	1.0	%	ISO 294-4
Flow	0.40	%	ISO 294-4
Water Absorption			ISO 62
Saturated, 23°C, 2.00mm	0.30	%	ISO 62
Balance, 23°C, 2.00mm, 50% RH	0.15	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5800	MPa	ISO 527-2
Tensile Stress (Break)	90.0	MPa	ISO 527-2
Tensile Strain (Break)	4.2	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	5400	MPa	ISO 899-1
1000 hr	3500	MPa	ISO 899-1

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	8.4	kJ/m²	ISO 179/1eA
23°C	10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	60	kJ/m²	ISO 179/1eU
23°C	55	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	180	°C	ISO 75-2/A
8.0 MPa, not annealed	120	°C	ISO 75-2/C
Vicat Softening Temperature	185	°C	ISO 306/B50
Melting Temperature ¹	205	°C	ISO 11357-3

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	> 1.0E+15	ohms·cm	IEC 60093
Dielectric Strength	27	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	4.10		IEC 60250
1 MHz	3.90		IEC 60250
Dissipation Factor			IEC 60250
100 Hz	0.012		IEC 60250
1 MHz	0.017		IEC 60250
Comparative Tracking Index	275	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94, IEC 60695-11-10, -20
1.5 mm	V-0		UL 94, IEC 60695-11-10, -20
3.0 mm	V-0		UL 94, IEC 60695-11-10, -20
Oxygen Index	30	%	ISO 4589-2
FMVSS Flammability	DNI		FMVSS 302

Fill Analysis	Nominal Value	Unit
Specific Heat Capacity of Melt	1850	J/kg/°C
Thermal Conductivity of Melt	0.25	W/m/K

Injection	Nominal Value	Unit
Melt Temperature, Optimum	250	°C
Mold Temperature, Optimum	80	°C
Back Pressure	As low as possible
Drying Recommended	yes
Hold Pressure Time	3.00	s/mm

Fill Analysis	Nominal Value	Unit
Melt Density	1.32	g/cm³
Ejection Temperature	150	°C

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time - Desiccant Dryer	2.0 - 4.0	hr
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	30 - 130	°C
Holding Pressure	60.0	MPa

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
VITAMIDE® BF13N2441/1	Jackdaw Polymers	Nylon 6	VITAMIDE®
Braskem PE LL218	Braskem	LLDPE	Braskem PE
ExxonMobil™ LLDPE LL 8555 Series	ExxonMobil Chemical	LLDPE	ExxonMobil™ LLDPE
ENGAGE™ 8207	The Dow Chemical Company	TPO (POE)	ENGAGE™
Sylvin 9302-70FU White 1346	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin