| EPO-TEK® 301 is a two component, room temperature curing epoxy featuring very low viscosity, and excellent optical-mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 65.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 3.9E-5 | cm/cm/°C | |
| -- 3 | 9.8E-5 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.519 | ||
| Transmittance | |||
| 380 to 980 nm | > 99.0 | % | |
| 980 to 1640 nm | > 97.0 | % | |
| 1640 to 2040 nm | > 95.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 20 | ||
| Part B | Mix Ratio by Weight: 5.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 430 | °C | TGA |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 2.26 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.12 | % | |
| 250°C | 0.13 | % | |
| 300°C | 0.39 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 0.868 | g/cm³ | |
| Part A | 1.15 | g/cm³ | |
| Viscosity 7(23°C) | 0.10 to 0.20 | Pa·s | |
| Curing Time (65°C) | 2.0 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 4.00 | ||
| Volume Resistivity (23°C) | > 1.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.016 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 30YM240 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| Salflex 620TIM | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Xuchuan XCS-2120A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Bynel® 1124 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| Chemlon® 66AR | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |