ASTALON™ K2000G2
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pYRzwt_ASTALON-K2000G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALON™ K2000G2 is a 10% Glass Filled flame retardant Polycarbonate that is designed to meet the stringent Underwriter's Laboratory UL94 V-0 test whilst offering improved rigidity, heat resistance, indoor colour stability and balance of impact toughness, product rigidity and mouldability. Typical applications include assemblies for electrical appliance and equipment. Other applications include metal substitution such as industrial electrical switch housings, electrical power tool casings and mounting chassis for electronics devices such as computer printers, laptop computers and VTR units. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 73.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 3350 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 25.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 144 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 136 | °C | |
| Vicat Softening Temperature | 158 | °C | ISO 306/A |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 245 to 260 | °C | |
| Middle Temperature | 255 to 270 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Processing (Melt) Temp | 265 to 280 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 30 to 50 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-3235 | Ravago Manufacturing Americas, LLC | PP Copolymer | Ravago Compounds |
| Vitaster® UR76WT6240 | Jackdaw Polymers | PBT | Vitaster® |
| XAREC™ SP130 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| UNISOFT TPE™ ST-55A-NT-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Lupoy® 1200-08 | LG Chem Ltd. | PC | Lupoy® |