Larpeek 10 K/40 HM
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larpeek |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pYDsNw_Larpeek-10-K-40-HM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyetheretherketone (PEEK). Carbon fibre. High modulus. Very good chemical resistance. Very good thermal resistance. Low smoke toxicity index and optical density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.25 to 0.45 | % | |
| Flow : 2.00 mm | 0.050 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 39500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 210 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.70 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 300 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 300 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 235 | °C | |
| Vicat Softening Temperature | > 300 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 370 to 400 | °C | |
| Mold Temperature | 170 to 200 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EM 2.8/58 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| VENYL UFRHG300R - 1335 | AD majoris | Nylon 66 | VENYL |
| Hanwha Total PP BJ300 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| HONES® Conductive Nylon | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon, Unspecified | HONES® |
| PENTAMID A GV40 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |